收縮率係指塑膠製品冷卻固化經脫模成形後,其尺寸與原模具尺寸間之誤差百分比,可依ASTM D955方法測得。在塑膠模具設計時,須先考慮收縮率,以免造成成品尺寸的誤差,導致成品不良。以下列舉幾項常用塑膠原料之收縮率比較。
熱塑性塑膠
塑料名稱
|
成形收縮率(%)
|
塑料名稱
|
成形收縮率(%)
|
ABS
|
0.3~0.8
|
PBT
|
1.3~2.4
|
AS
|
0.2~0.7
|
PC
|
0.4~0.7
|
CA
|
0.3~0.8
|
PCTFE
|
0.2~2.5
|
CAB
|
0.4~0.5
|
PE
|
0.5~2.5
|
CAP
|
1
|
PET
|
2.0~2.5
|
CP
|
0.4~0.5
|
PES
|
0.5~1.0
|
EC
|
0.4~0.5
|
PMMA
|
0.2~0.8
|
EPS
|
0.4
|
POM
|
0.8~3.5
|
FEP
|
3.0~4.0
|
PP
|
1.0~2.5
|
FRP
|
0.1~0.4
|
PPO
|
0.5~0.7
|
EVA
|
0.5~1.5
|
PPS
|
0.6~1.4
|
HDPE
|
1.2~2.2
|
PS
|
0.2~1.0
|
HIPS
|
0.2~1.0
|
PVA
|
0.5~1.5
|
LCP
|
0.1~1.0
|
PVAC
|
0.5~1.5
|
LDPE
|
1.5~3.0
|
PVB
|
0.5~1.5
|
PA
|
0.6~2.5
|
硬質PVC
|
0.1~0.5
|
PA-6
|
0.5~2.2
|
軟質PVC
|
1.0~5.0
|
PA-66
|
0.5~2.5
|
PVCA
|
1.0~5.0
|
PA-610
|
1.2
|
PVDC
|
0.5~2.5
|
PA-612
|
1.1
|
PVFM
|
0.5~1.5
|
PA-11
|
1.2
|
SAN
|
0.2~0.6
|
PA-12
|
0.3~1.5
|
SB
|
0.2~1.0
|
PAR
|
0.8~1.0
|
|
|
熱固性塑膠
塑料名稱
|
成形收縮率(%)
|
塑料名稱
|
成形收縮率(%)
|
EP
|
0.1~0.5
|
SP
|
0.0~0.5
|
MF
|
0.5~1.5
|
UF
|
0.6~1.4
|
PDAP
|
0.1~0.5
|
UP
|
0.1~1.2
|
PF
|
0.4~0.9
|
DAP
|
0.1~0.5
|
PU
|
0.6~0.8
|
BMC
|
0.0~0.2
|
|